Comparative analysis of union resistance of Y-TZP ceramics to bovine dentina by means of surface treatments
DOI:
https://doi.org/10.55892/jrg.v7i15.1592Keywords:
Ceramic, Cementation, Dental materialsAbstract
Hypotheses of study: The increase in the crystalline content of Yttrium stabilized tetragonal zirconia polycrystal (Y-TZP) ceramics modified their adhesion characteristics with resin cements and dental structure, and there was no well-established cementation protocol in the literature for adhesion between these elements effective. Objective: This work was analysed the bond strength of cemented Y-TZP zirconia to the bovine dentin by means of a micro-shear test, correlating two different types of surface treatments: sandblasting with aluminum oxide and application of hydrofluoric acid to 10%. Methodology: Twenty sintered Y-TZP zirconia blocks were divided into two groups and submitted to different surface treatments. Group 1 (G1) (n = 10) was treated by blasting with aluminum oxide AL3O2 under a loading pressure of 1 Bar and average particle sizes of 110 micrometers (ROCATEC Plus - 3M - São Carlos, Brazil). Group 2 (G2), received 10% hydrofluoric acid as a surface treatment. The treated blocks were cemented to trimmed bovine teeth, preserving both dentin and enamel structure. The micro-shear test on the teeth / samples set (Instron, Canton, Massachusetts, USA) were performed and the test specimens were analyzed. Results: A Statistical analysis was performed initially by the Kolmogorov-Smirnov test. A Student t test with significance values (p> 0.05) was used to compare the groups for the mean of the Strength, Maximum Load and the correlation between the groups the test of Person. Conclusion: there is a statistically significant mean difference between the groups (G1 and G2) for both the Resistance and the Maximum Load. In both variables the mean is higher in Group 1 than in Group 2. Both groups were positive, indicating that the higher the resistance, the higher the maximum load for each other group. In addition, the failures found in all groups were adhesive type.
Downloads
References
Alghazzawi TF, Lemons J, Liu PR, Essig ME, Janowski GM. The failure load of CAM/CAM generated zircônia and glass-ceramic laminate veneers with diferente preparation designs. Journal of Prosthetic Dentistry 2012; 108:386-393.
Aras, Wanessa Maria de Freitas; Ferreira, Alessandra Cassoni. Avaliação de tratamentos de superfície de zircônia para cimentação adesiva. 57 f. Tese (Doutorado), Universidade de Guarulhos, Guarulhos-sp, 2015.
Blatz MB, Chiche G, Holst S, Sadan A. Influence of surface treatment and simulated aging on bond strengths of luting agents to zirconia. Quintessence Int 2007; 38:745-53.
Carvalho, Juliana Souza; GIANNINI, Marcelo; CAVALCANTI, Andrea Nóbrega. Durabilidade da união à cerâmica de zircônia tetragonal poli cristalina contendo ítrio (y-tzp). Revista Bahiana de Odontologia, Salvador, v. 3, n. 1, p.27-44, dez. 2012.
Chen, J.h.; Matsumura, H.; Matsuta, M. Effect of different etching periods on the bond strength of a composite resin to a machinable porcelain. Journal of Dentistry. Nagasaki, Japan, p. 53-58. 21 out. 1996.
Della Bona A, Borba M, Benetti P, Cecchetti D. Effect of surface treatments on the bond strength of a zirconia-reinforced ceramic to composite resin. Braz Oral Res 2007; 21:10-5.
Dias, Tiago Monteiro et al. Avaliação do efeito da aplicação de primers para metal e do tipo de cimento resinoso na resistência de união à zircônia. Revista Brasileira de Odontologia, Rio de Janeiro, v. 69, n. 1, p.15-21, Jan./Jun. 2012
Diniz, Alexandre C. et al. Fracture and shear bond strength analyses of different dental veneering ceramics to zirconia. Materials Science And Engineering, Natal, v. 38, n. 1, p.79-84, jan. 2014.
Fischer, Jens et al. Impact of thermal misfit on shear strength of veneering ceramic/zirconia composites. Academy Of Dental Materials, Zurich, v. 25, n. 1, p.419-423, set. 2008.
Goyatá, Frederico dos Reis. Avaliação de parâmetros clínicos relacionados com a longevidade de restaurações cerâmicas livres de meta. 98 f. Tese (Doutorado), Universidade de Taubaté, Taubaté - Sp, 2010.
Kelly J. R.; Denry I. Stabilized zirconia as a structural ceramic: an overview. Dental Materials, v. 24, n. 3, p. 289-298, Mar 2008.
Lago, Carlo Theodoro Raymundi; BARATIERI, Luiz Narciso. Resistência adesiva a uma cerâmica à base de zircônia – influência do tipo de primer para cerâmica. 81 f. Dissertação (Mestrado), Universidade Federal de Santa Catarina, Florianópolis, 2011.
Luthardt, R.g. et al. Reliability and Properties of Ground Y-TZP-Zirconia Ceramics. Journal of Dental Research, [s.l.], v. 81, n. 7, p.487-491, Jul. 2002. SAGE Publications. http://dx.doi.org/10.1177/154405910208100711.
Maeda, Fernando Akio. Avaliação da influência de diferentes tratamentos de superfície na resistência de união ao cisalhamento entre zircônia Y-TZP e o cimento resinoso. 68 f. Tese (Doutorado), Faculdade de Odontologia da Universidade de São Paulo, São Paulo, 2012.
Melo, Andréa Silva de Matos. Caracterização microestrutual de zirconia micro e nanoparticulada e análise das propriedades mecânicas de próteses usinadas em CAD/CAM. 91 f. Dissertação (Mestrado), Instituto Militar de Engenharia, Rio de Janeiro, 2010.Prieto, Lúcia Trazzi. Análise de sistemas de fixação resinosos: por meio de nanoinfiltração, microdureza e micro cisalhamento. 83 f. Dissertação (Mestrado), Universidade Estadual de Campinas, Piracicaba, Sp, 2011.
Mudado, Flávia Amata. Cimentação adesiva ceramicas a base de zirconia. 60 f. Monografia (Especialização), Faculdade de Odontologia da Universidade Federal de Minas Gerais, Belo Horizonte, 2012.
Nakamichi, J., Waku, M., Fusayama, T. Bovine teeth as possible substitutes in the adhesion tests. J. Dent. Res., v.62, n.l O, p. 1076-8 1, Oct. !983
Peçanha, Marcelo Massaroni; Concilio, Laís Regiane da Silva. Influência de diferentes tratamentos de superfícies e agentes de cimentação no processo de adesão de um sistema cerâmico à base de zircônia. 83 f. Tese (Doutorado), Universidade de Taubaté, Taubaté, 2013.
Pittayachawan P, McDonald A, Petrie A, Knowles JC. The biaxial flexural strength and fatigue property of Lava Y-TZP dental ceramic. Dent Mater 2007; 23:1018-29.
Prieto, Lúcia Trazzi. Análise de sistemas de fixação resinosos: por meio de nanoinfiltração, microdureza e micro cisalhamento. 83 f. Dissertação (Mestrado), Universidade Estadual de Campinas, Piracicaba, Sp, 2011.
Qeblawi M.D., Monöz C.A., Brewer J.D., Monaco E.A. The effect of zirconia surface traetment on flexural strength and shear bond strength to a resin cement. J. Prosthet. Dent. v.103, n.4, p.210-20, 2010.
Ribeiro, José Carlos Viana; Valei M. S; Silva M. M; Fernandes C A O. Ensaio de micro tração na avaliação da resistência adesiva: fundamentos e aplicações. Revista Gaúcha de Odontologia, Porto Alegre, v. 61, n. 0, p.497-504, jul/dez. 2013.
Santos, Livia Aguiar. Avaliação da resistência ao cisalhamento da zircônia após diferentes tratamentos de superfície. 107 f. Dissertação (Mestrado), Faculdade de Odontologia de Bauru, Bauru-sp, 2011.
Santos, R.l.p. et al. Shear bond strength of veneering porcelain to zirconia: Effect of surface treatment by CNC-milling and composite layer deposition on zirconia. Journal Of The Mechanical Behavior Of Biomedical Materials, [s.l.], v. 60,p. 547-556,Jul. 2016. Elsevier BV. http://dx.doi.org/10.1016/j.jmbbm.2016.03.015.
95 Saunders, W. P. The shear impact retentive strengths of four dentine bonding agents to human and bovine dentine. J. Dent., v.16, p.223-8, 1988.
Silva, Isabela da Rocha; Concilio, Laís Regiane da Silva. Avaliação da resistência de união da interface cerâmica Y-TZP/dentina humana utilizando diferentes agentes de cimentação e tratamentos de superfície. 77 f. Dissertação (Mestrado), Universidade de Taubaté, Taubaté, 2015.
Thompson, Jeffrey Y. et al. Adhesion/cementation to zirconia and other non-silicate ceramics: Where are we now? Dental Materials, [s.l.], v. 27, n. 1, p.71-82, Jan. 2011. Elsevier BV. http://dx.doi.org/10.1016/j.dental.2010.10.022.
Vasconcelos, Urias Silva; Moura, Carmem Dolores Vilarinho Soares de. Efeito de diferentes tratamentos de superfície da zircônia na resistência ao cisalhamento da cimentação resinosa. 81 f. Dissertação (Mestrado), Universidade Federal do Piauí, Teresina, 2016.